EnvisionTEC

  • D4K Pro Dental

    D4K Pro Dental

    Introducing the D4K Pro, the highest resolution 4K desktop 3D printer. The D4K Pro from EnvisionTEC includes the fastest print speed for a standard DLP printer, and delivers extremely accurate parts...

    Log in for pricing

  • E - AquaModel E - AquaModel

    E - AquaModel

    EnvisionTEC’s groundbreaking E-AquaModel printing material for DLP and cDLM 3D printers is the perfect choice for high-accuracy orthodontic models ans well as solid crown and bridge models...

    Log in for pricing

  • Flexural Strength

158 MPa

Flexural Modulus

4790 MPa

Vickers Hardness

33 HV
PCA 4000

    E-MFP

    E-MFP (Metal Free Partial) is a revolutionary dental material able to be used in the production of ready-to-use partial denture. No need for casting and assembling, dental professionals will be able...

    Log in for pricing

  • Viscosity @ 30°C

535 cP

Young's Modulus, Dry Material

780 MPa

Young's Modulus, After Immersion in Water for 2 Days -37°C

902 MPa

Ultimate Strength, Dry Material

37.4 MPa

Ultimate Strength, After Immersion in Water for 2 Days -37°C

45.8 MPa

Strain at Break, Dry Material

76%

Strain at Break, After Immersion in Water for 2 Days -37°C

58.5%

Ultimate Flexural Strength, Dry Material

90 MPa

Ultimate Flexural Strength, After Immersion in Water for 2 Days -37°C

81 MPa

Flexural Modulus, Dry Material

2380 MPa

Flexural Modulus, After Immersion in Water for 2 Days -37°C

2325 MPa

Shore D

81

Izod Notched Impact

29.6 J/m

Total Work Fracture

3500 J/m2

PCA 4000

    Flexcera BaseMFP ( Dark Meharry )

    Flexcera Base is a light-curable resin for the fabrication of high-impact and removable denture bases. Introducing Flexcera™, a new resin for the fabrication of beautiful, functional...

    Log in for pricing

  • Viscosity @ 30°C

535 cP

Young's Modulus, Dry Material

780 MPa

Young's Modulus, After Immersion in Water for 2 Days -37°C

902 MPa

Ultimate Strength, Dry Material

37.4 MPa

Ultimate Strength, After Immersion in Water for 2 Days -37°C

45.8 MPa

Strain at Break, Dry Material

76%

Strain at Break, After Immersion in Water for 2 Days -37°C

58.5%

Ultimate Flexural Strength, Dry Material

90 MPa

Ultimate Flexural Strength, After Immersion in Water for 2 Days -37°C

81 MPa

Flexural Modulus, Dry Material

2380 MPa

Flexural Modulus, After Immersion in Water for 2 Days -37°C

2325 MPa

Shore D

81

Izod Notched Impact

29.6 J/m

Total Work Fracture

3500 J/m2

PCA 4000

    Flexcera BaseMFP ( Dark Pink )

    Flexcera Base is a light-curable resin for the fabrication of high-impact and removable denture bases. Introducing Flexcera™, a new resin for the fabrication of beautiful, functional...

    Log in for pricing

  • Viscosity @ 30°C

535 cP

Young's Modulus, Dry Material

780 MPa

Young's Modulus, After Immersion in Water for 2 Days -37°C

902 MPa

Ultimate Strength, Dry Material

37.4 MPa

Ultimate Strength, After Immersion in Water for 2 Days -37°C

45.8 MPa

Strain at Break, Dry Material

76%

Strain at Break, After Immersion in Water for 2 Days -37°C

58.5%

Ultimate Flexural Strength, Dry Material

90 MPa

Ultimate Flexural Strength, After Immersion in Water for 2 Days -37°C

81 MPa

Flexural Modulus, Dry Material

2380 MPa

Flexural Modulus, After Immersion in Water for 2 Days -37°C

2325 MPa

Shore D

81

Izod Notched Impact

29.6 J/m

Total Work Fracture

3500 J/m2

PCA 4000

    Flexcera BaseMFP ( Light Pink )

    Flexcera Base is a light-curable resin for the fabrication of high-impact and removable denture bases. Introducing Flexcera™, a new resin for the fabrication of beautiful, functional...

    Log in for pricing

  • Viscosity @ 30°C

535 cP

Young's Modulus, Dry Material

780 MPa

Young's Modulus, After Immersion in Water for 2 Days -37°C

902 MPa

Ultimate Strength, Dry Material

37.4 MPa

Ultimate Strength, After Immersion in Water for 2 Days -37°C

45.8 MPa

Strain at Break, Dry Material

76%

Strain at Break, After Immersion in Water for 2 Days -37°C

58.5%

Ultimate Flexural Strength, Dry Material

90 MPa

Ultimate Flexural Strength, After Immersion in Water for 2 Days -37°C

81 MPa

Flexural Modulus, Dry Material

2380 MPa

Flexural Modulus, After Immersion in Water for 2 Days -37°C

2325 MPa

Shore D

81

Izod Notched Impact

29.6 J/m

Total Work Fracture

3500 J/m2

PCA 4000

    Flexcera BaseMFP ( Medium Pink )

    Flexcera Base is a light-curable resin for the fabrication of high-impact and removable denture bases. Introducing Flexcera™, a new resin for the fabrication of beautiful, functional...

    Log in for pricing

  • Viscosity @ 30°C

535 cP

Young's Modulus, Dry Material

780 MPa

Young's Modulus, After Immersion in Water for 2 Days -37°C

902 MPa

Ultimate Strength, Dry Material

37.4 MPa

Ultimate Strength, After Immersion in Water for 2 Days -37°C

45.8 MPa

Strain at Break, Dry Material

76%

Strain at Break, After Immersion in Water for 2 Days -37°C

58.5%

Ultimate Flexural Strength, Dry Material

90 MPa

Ultimate Flexural Strength, After Immersion in Water for 2 Days -37°C

81 MPa

Flexural Modulus, Dry Material

2380 MPa

Flexural Modulus, After Immersion in Water for 2 Days -37°C

2325 MPa

Shore D

81

Izod Notched Impact

29.6 J/m

Total Work Fracture

3500 J/m2

PCA 4000

    Flexcera BaseMFP ( Original Pink )

    Flexcera Base is a light-curable resin for the fabrication of high-impact and removable denture bases. Introducing Flexcera™, a new resin for the fabrication of beautiful, functional...

    Log in for pricing

  • Viscosity @ 30°C

660 cP

Shore D

89-90

Izod Notched Impact

20 J/m

Heat Deflection Temperature

58°C @ 1.82 MPa

Vickers Hardness

18 HV

Young's Modulus, Dry Material

1340 MPa

Young's Modulus, After Immersion in Water 2 Days -37°C

1330 MPa

Ultimate Strength, Dry Material

67.5 MPa

Ultimate Strength, After Immersion in Water 2 Days -37°C

68.9 MPa

Strain at Break, Dry Material

16%

Strain at Break, After Immersion in Water 2 Days -37°C

14%

Ultimate Flexural Strength, Dry Material

136 MPa

Ultimate Flexural Strength, After Immersion in Water 2 Days -37°C

120 MPa

Flexural Modulus, Dry Material

3660 MPa

Flexural Modulus, After Immersion in Water 2 Days -37°C

3300 MPa

Envision One cDLM Dental, D4K Pro Dental, PCA 4000

    Flexcera Smile ( A1 )

    Light-curable resin for the fabrication of high-impact artificial teeth with variable translucency for dentures. Compatible and validated for use with EnvisionTEC™ systems.

    Log in for pricing

  • Viscosity @ 30°C

660 cP

Shore D

89-90

Izod Notched Impact

20 J/m

Heat Deflection Temperature

58°C @ 1.82 MPa

Vickers Hardness

18 HV

Young's Modulus, Dry Material

1340 MPa

Young's Modulus, After Immersion in Water 2 Days -37°C

1330 MPa

Ultimate Strength, Dry Material

67.5 MPa

Ultimate Strength, After Immersion in Water 2 Days -37°C

68.9 MPa

Strain at Break, Dry Material

16%

Strain at Break, After Immersion in Water 2 Days -37°C

14%

Ultimate Flexural Strength, Dry Material

136 MPa

Ultimate Flexural Strength, After Immersion in Water 2 Days -37°C

120 MPa

Flexural Modulus, Dry Material

3660 MPa

Flexural Modulus, After Immersion in Water 2 Days -37°C

3300 MPa

Envision One cDLM Dental, D4K Pro Dental, PCA 4000

    Flexcera Smile ( A2)

    Light-curable resin for the fabrication of high-impact artificial teeth with variable translucency for dentures. Compatible and validated for use with EnvisionTEC™ systems.

    Log in for pricing

  • Viscosity @ 30°C

660 cP

Shore D

89-90

Izod Notched Impact

20 J/m

Heat Deflection Temperature

58°C @ 1.82 MPa

Vickers Hardness

18 HV

Young's Modulus, Dry Material

1340 MPa

Young's Modulus, After Immersion in Water 2 Days -37°C

1330 MPa

Ultimate Strength, Dry Material

67.5 MPa

Ultimate Strength, After Immersion in Water 2 Days -37°C

68.9 MPa

Strain at Break, Dry Material

16%

Strain at Break, After Immersion in Water 2 Days -37°C

14%

Ultimate Flexural Strength, Dry Material

136 MPa

Ultimate Flexural Strength, After Immersion in Water 2 Days -37°C

120 MPa

Flexural Modulus, Dry Material

3660 MPa

Flexural Modulus, After Immersion in Water 2 Days -37°C

3300 MPa

Envision One cDLM Dental, D4K Pro Dental, PCA 4000

    Flexcera Smile ( A3)

    Light-curable resin for the fabrication of high-impact artificial teeth with variable translucency for dentures. Compatible and validated for use with EnvisionTEC™ systems.

    Log in for pricing

  • Viscosity @ 30°C

660 cP

Shore D

89-90

Izod Notched Impact

20 J/m

Heat Deflection Temperature

58°C @ 1.82 MPa

Vickers Hardness

18 HV

Young's Modulus, Dry Material

1340 MPa

Young's Modulus, After Immersion in Water 2 Days -37°C

1330 MPa

Ultimate Strength, Dry Material

67.5 MPa

Ultimate Strength, After Immersion in Water 2 Days -37°C

68.9 MPa

Strain at Break, Dry Material

16%

Strain at Break, After Immersion in Water 2 Days -37°C

14%

Ultimate Flexural Strength, Dry Material

136 MPa

Ultimate Flexural Strength, After Immersion in Water 2 Days -37°C

120 MPa

Flexural Modulus, Dry Material

3660 MPa

Flexural Modulus, After Immersion in Water 2 Days -37°C

3300 MPa

Envision One cDLM Dental, D4K Pro Dental, PCA 4000

    Flexcera Smile ( A3.5)

    Light-curable resin for the fabrication of high-impact artificial teeth with variable translucency for dentures. Compatible and validated for use with EnvisionTEC™ systems.

    Log in for pricing

  • Viscosity @ 30°C

660 cP

Shore D

89-90

Izod Notched Impact

20 J/m

Heat Deflection Temperature

58°C @ 1.82 MPa

Vickers Hardness

18 HV

Young's Modulus, Dry Material

1340 MPa

Young's Modulus, After Immersion in Water 2 Days -37°C

1330 MPa

Ultimate Strength, Dry Material

67.5 MPa

Ultimate Strength, After Immersion in Water 2 Days -37°C

68.9 MPa

Strain at Break, Dry Material

16%

Strain at Break, After Immersion in Water 2 Days -37°C

14%

Ultimate Flexural Strength, Dry Material

136 MPa

Ultimate Flexural Strength, After Immersion in Water 2 Days -37°C

120 MPa

Flexural Modulus, Dry Material

3660 MPa

Flexural Modulus, After Immersion in Water 2 Days -37°C

3300 MPa

Envision One cDLM Dental, D4K Pro Dental, PCA 4000

    Flexcera Smile ( B1 )

    Light-curable resin for the fabrication of high-impact artificial teeth with variable translucency for dentures. Compatible and validated for use with EnvisionTEC™ systems.

    Log in for pricing

  • Viscosity @ 30°C

660 cP

Shore D

89-90

Izod Notched Impact

20 J/m

Heat Deflection Temperature

58°C @ 1.82 MPa

Vickers Hardness

18 HV

Young's Modulus, Dry Material

1340 MPa

Young's Modulus, After Immersion in Water 2 Days -37°C

1330 MPa

Ultimate Strength, Dry Material

67.5 MPa

Ultimate Strength, After Immersion in Water 2 Days -37°C

68.9 MPa

Strain at Break, Dry Material

16%

Strain at Break, After Immersion in Water 2 Days -37°C

14%

Ultimate Flexural Strength, Dry Material

136 MPa

Ultimate Flexural Strength, After Immersion in Water 2 Days -37°C

120 MPa

Flexural Modulus, Dry Material

3660 MPa

Flexural Modulus, After Immersion in Water 2 Days -37°C

3300 MPa

Envision One cDLM Dental, D4K Pro Dental, PCA 4000

    Flexcera Smile ( Bleach )

    Light-curable resin for the fabrication of high-impact artificial teeth with variable translucency for dentures. Compatible and validated for use with EnvisionTEC™ systems.

    Log in for pricing

  • E1 - Guard 2.0

    E1 - Guard 2.0

    EnvisionTEC’s E-Guide is a biocompatible certified Class I material, developed for the production of high precision surgical drill guides for use in implant surgery. The results produced by...

    Log in for pricing